Styrene-Acrylic Resins

Styrene-Acrylic Resins ＜Emulsion＞

Characteristics

By using the core-shell technology (i.e. combination of the insoluble core and the water soluble shell), the compatibility of the property of water soluble polymer and that of emulsion polymer can be achieved.
Emulsification polymerization technology provides high performance products.
By grafting the shell resin, it is possible to realize improved performance such as higher resistance to water / oil / alcohol and better mechanical / freezing stability.
These resins provide excellent stability and good physical properties.

Please inquire about Inventory registration of emulsion products.
These products described blow are just typical examples from our product range. We also have many other resins available.

↓ Please scroll to the side to see.

Product name	Non-volatile （%）	Viscosity （mPa・s）	pH	Mean particle size （nm）	Acid value　(theoretical value)	Tg (℃) (theoretical value)	MFT^* （℃）	Characteristics	Remarks
TE-1048	31.0	800	8.0	250	200	123	55	Heat resistance	IPA(9％)
PE-1304	33.0	600	8.5	250	142	9	<5	Heat resistance, Film-formability, Adhesion to unaborbed materials	ethanol（8%）
X-436	40.0	200	8.5	40	33	21	<5	Pigment dispersion, High Perfomance balance
QE-1042	40.5	200	8.5	40	33	53	45	Adhesion to unaborbed materials, Heat resistance, Blocking resistance
J-140A	41.0	170	8.5	60	33	6	<5	Adhesion to unaborbed materials, Film strength, Rub resistance, Laminating property	ethanol（2%）
KE-1062	43.0	1,200	8.5	80	149	96	55	Heat resistance, Blocking resistance
HE-1335	45.5	700	8.5	90	84	15	<5	High gloss,Water resistance, Rub resistance
KE-1060	46.0	1,200	8.0	80	100	16	<5	Quickly drying, High gloss, Blocking resistance
RE-1075	47.0	800	8.5	100	100	15	<5	Rub resistance, Film-formability, High gloss

(*) minimum film forming temperature

↓ Please scroll to the side to see.

Product name	Non-volatile （%）	Viscosity （mPa・s）	pH	Mean particle size （nm）	Acid value　(theoretical value)	Tg (℃) (theoretical value)	MFT^* （℃）	Characteristics
PE-1126	41.5	1,100	8.5	60	50	-12	<5	Self-crosslinking, Adhesion to unaborbed materials, Redissolvability
JE-1056	42.5	200	8.5	50	25	82	>80	Heat resistance, Blocking resistance, Light resistance
JE-1113	42.5	300	8.1	60	42	-24	<5	Adhesion to unaborbed materials, Water resistance, Redissolvability
KE-1148	43.0	250	8.5	80	31	21	<5	Redissolvability, Rub resistance, Coloring
M-141	45.0	750	9.0	70	19	15	<5	Adhesion to unaborbed materials, Water / oil resistance, Film strength, Flexibility

(*) minimum film forming temperature