Products Information

Emulsion-Product List

Styrene-Acrylic Resin

Product list

Product name Non-volatile (%) Viscosity (mPa・s) pH Mean particle size (nm) Acid value (theoretical value) Tg (℃) (theoretical value) MFT*
(℃)
Characteristics Remarks
TE-1048 31.0 800 8.0 250 200 123 55 Heat resistance IPA(9%)
PE-1304 33.0 600 8.5 250 142 9 <5 Heat resistance,
Film-formability,
Adhesion to unaborbed materials
ethanol(8%)
X-436 40.0 200 8.5 40 33 21 <5 Pigment dispersion,
High Perfomance balance
 
QE-1042 40.5 200
8.5 40 33 53 45 Adhesion to unaborbed materials,
Heat resistance,
Blocking resistance
 
J-140A 41.0 170 8.5 60 33 6 <5 Adhesion to unaborbed materials,
Film strength,
Rub resistance,
Laminating property
ethanol(2%)
KE-1062 43.0 1,200 8.5 80 149 96 55 Heat resistance,
Blocking resistance
 
HE-1335 45.5 700 8.5 90 84 15 <5 High gloss,
Water resistance,
Rub resistance
 
KE-1060 46.0 1,200 8.0 80 100 16 <5 Quickly drying,
High gloss,
Blocking resistance
 
RE-1075 47.0 800 8.5 100 100 15 <5 Rub resistance,
Film-formability,
High gloss
 

(*) minimum film forming temperature

Please inquire about Inventory registration of emulsion products.

These products are just typical examples from our product range. We also have many other resins available.

Acrylic Resin

Product list

Product name Non-volatile (%) Viscosity (mPa・s) pH Mean particle size (nm) Acid value (theoretical value) Tg (℃) (theoretical value) MFT*
(℃)
Characteristics
PE-1126 41.5 1,100 8.5 60 50 -12 <5 Self-crosslinking,
Adhesion to unaborbed materials,
Redissolvability
JE-1056 42.5 200 8.5 50 25 82 >80 Heat resistance,
Blocking resistance,
Light resistance
JE-1113 42.5 300 8.1 60 42 -24 <5 Adhesion to unaborbed materials,
Water resistance,
Redissolvability
KE-1148 43.0 250 8.5 80 31 21 <5 Redissolvability,
Rub resistance,
Coloring
M-141 45.0 750 9.0 70 19 15 <5 Adhesion to unaborbed materials,
Water / oil resistance,
Film strength,
Flexibility

(*) minimum film forming temperature

Please inquire about Inventory registration of emulsion products.

These products are just typical examples from our product range. We also have many other resins available.

Functional Cotting Agent

Moisture-Proofness・Water Resistant Emulsion

Product name Non-volatile (%) Viscosity (mPa・s) pH Mean particle size (nm) Acid value (theoretical value) Tg (℃) (theoretical value) MFT*
(℃)
Characteristics
XP8812 41.0 500 9.0 50 61 -9 <5 Moisture-proofness,
Water resistance

(*) minimum film forming temperature

Water/Grease-proof Emulsion【Development Article】

Product name Non-volatile (%) Viscosity (mPa・s) pH Mean particle size (nm) Acid value (theoretical value) Tg (℃) (theoretical value) MFT*
(℃)
Characteristics
NE-2260 49.0 600 8.0 90 53 -10 <5 176.170 Application limited
176.180 Confirm

(*) minimum film forming temperature

Vinylchloride/Acrylic Emulsion【Development Article】

Product name Non-volatile (%) Viscosity (mPa・s) pH Mean particle size (nm) Acid value (theoretical value) Tg (℃) (theoretical value) MFT*
(℃)
Characteristics Remarks
PVC content
BE-7500 30.0 400 8.0 65 45 38 <5 Pigment dispersion,
Rub resistance
50%
BE-7650 30.0 150 8.0 30 31 53 <5 Rub resistance 65%
BE-7502 30.0 200 8.0 80 45 15 <5 Adhesion to substrates 40%
BE-7503 30.0 50 MAX 8.0 50 50 56 <5 Alcohol resistance 50%

(*) minimum film forming temperature

Vinylchloride/Acrylic Emulsion is that Products of joint development with Nissin Chemical Industry Co.,Ltd

Biomass Emulsion【Development Article】

Product name Non-volatile (%) Viscosity (mPa・s) pH Mean particle size (nm) Acid value (theoretical value) Biomass MFT*
(℃)
Characteristics Biomass content
PE-2027 45.0 960 8.2 200 5 Starch <5 Solvent resistance 50%
PE-2189 45.0 600 8.3 100 155 Rosin <5 Wet rub resistance,
High gloss
50%
NE-2309 40.0 800 8.5 60 51 Fatty acid <5 Adhesive PET/PP/PS film 20%

(*) minimum film forming temperature